Effect of fly and dust ash additions on hardness and wear resistance of composite metal matrix (Al-Si-Mg)‎

الملخص EN

The current paper deals with the preparation of bars with a length of about 13 cm and 2.5 cm diameter from MMC materials.

These composites consists of cast (Al-Si-Mg) as a matrix that reinforced with fly ash (0.454 μm) or fly dust (0.620 μm) in relative weights (2, 4, 6, and 8 %) respectively.

Both of composite materials samples were manufactured by casting method (Vortex method).

Vortex method has been used successfully to obtain a homogeneous distribution of reinforcement particles.

Samples were classified into two categories according to the type of reinforcement particles.

The results showed that the wear rate of the samples depends heavily on the working conditions.

Which increases with increased load and download time? The results also showed superiority aluminum alloy reinforced fly ash compared with the aluminum alloy reinforced with dust flying.

Furthermore, a significant increase in the hardness and wear resistance for all samples prepared with increasing added particles for the purpose of reinforcement.