The role of Ta and Nb additions on the transformation temperature of NITI shape memory alloy

مقدم أطروحة جامعية

Husayn, Rasha Ali

مشرف أطروحة جامعية

al-Saffar, Sahib Mahdi
al-Hasani, Imad Sadi

الجامعة

الجامعة التكنولوجية

الكلية

-

القسم الأكاديمي

قسم هندسة المواد

دولة الجامعة

العراق

الدرجة العلمية

ماجستير

تاريخ الدرجة العلمية

2011

الملخص الإنجليزي

-The aim of the present study is to prepare NiTi alloys as references alloy and NiTi alloys with different additives of Ta and Nb individually, then, do a comparison between the characteristics of each group.

The purpose of experimenting the physical characteristics and transformation temperatures of alloys is to elect the better percentage of additives for different applications.Powder technology technique is used to prepare the samples; the temperature of sintering was 950 °C at time 9 hr.

The prepared samples were Master sample M1 55 wt% Ni-45 wt% Ti and master sample M2 56 wt% Ni-44 wt% Ti.

The additive of Ta was 5%, 7% and 9% to master sample M1 and M2, while Nb addition was 1%, 2% and 4% to M1 and M2.

The pressure used was 800 MPa.

After samples preparation, they have been examined by using SEM technique, XRD, DSC, Vickers hardness and Archimedes method in measuring the porosity percentage.

Scanning electron microscopy analysis determines that most prepared samples have porosity, which in turn imparts decreasing microhardness values across the surface.

Better increase of microhardness values is found in T2 (M2+5%Ta).

Scanning electron observations indicated also the best martensitic structure in N5 (M1+4% Nb) and N6 (M2+4%Nb).

X-ray diffraction observations indicated that NiTi phases, Ni3Ti phases and NiTi2 phases exist in all samples.

NiTi phase plays a dramatic role in enhancing shape memory effect and superelasticity.

DSC results show that transformation temperatures range is in 46-134°C; this indicates that all samples at room temperature (~30 °C) have one phase which is martensite.

Hardness and Porosity results show that M2 has more hardness and less porosity than M1, and addition of Ta and Nb mostly lead to increase in porosity and decrease in hardness.