Corrosion performance of copper coated with carbon nanotubes

الملخص EN

A thick layer of multi-wall carbon nanotubes (CNTs) was deposited on a copper surface by gravity from a solution containing dispersed CNTs in water.

Scanning electron microscopy (SEM) was utilized to characterize the morphology, uniformity, and thickness of the CNT coating.

A low magnification examination shows a uniform coating.

However, a closer look at the SEM images reveals that the coating consists of clumps of CNTs deposited rather irregularly on the surface.

The Vickers micro hardness values measured using a 300 gf load for copper (Cu) and CNT coated Cu samples were 104 and 111 HV, respectively.

This indicates that the CNT coating provided a slightly harder surface than Cu substrate.

A corrosion test was carried out in salted water (3wt concentration) to investigate the effect of CNT coating on the corrosion performance of copper.

The corrosion resistance (Rp) calculated from the linear polarization resistance results yielded 585 Ohms for Cu and 26,460 Ohms for the CNT coated Cu, indicating a drastic increase in the corrosion resistance of about 45 times.

In other words, the corrosion rate of Cu has been greatly reduced by the deposited CNT coating, thus allowing a potentially longer lifetime.