Structure rheology of polyethylene oxide solution

الملخص EN

Intrinsic viscosities have been studied for polyethylene oxide in water which has wide industrial applications.

The polyethylene oxide samples had two different structures, the first one was linear and covers a wide range of molecular weight of 1, 3, 10, 20, 35, 99, 370, 1100, 4600, and 8000 kg / mol and the second one was branched and had molecular weights of 0.55 and 40 kg / mol.

Intrinsic viscosities and Huggins constants have been determined for all types and molecular weights mentioned above at 25ºC using a capillary viscometer.

The values of Mark-Houwink parameters (K and a) were equal to 0.0068 ml / g and 0.67 respectively, and have not been published for this range of molecular weight in as yet.