On fatigue crack propagation in HSLA steels

الملخص EN

-Corrosion fatigue crack growth rates in 3.

5 % NaCI water solution have been investigated on high tensile low alloy steel used for mining chains.

The aim of this study is to show the effect of a corrosive environment on the relationship between the Paris-Erdogan (C and n).

It is found that a linear behavior is obtained in air and corrosive environment.

Meanwhile the fatigue corrosion process results in increasing values of C by a factor of 10 for the same value of n in air.

This finding is confirmed using data from literature for 35 NCD 16, SAE 51100 steels.

Keywords: high tensile steel, fatigue, corrosion, crack propagation, K(stc RESUME Les vitesses des fissures en fatigue ont fait Pobjet d’titude dans un environnement corrosif, compost d’une solution d’eau & 3.

15 % de NaCI.

L’objectif de ce travail est de monter I’influence de la corrosion sur les parametres C et n de la loi de Paris-Erdogan.

II en resulte que la relation est lineaire dans deux conditions d’essais, air et corrosion.

Cependant les valeurs de C obtenues dans la corrosion sont augmentees de 10 pour la meme valeur de n prise dans Pair.

En analysant les resultats donnds par la litterature pour des aciers de