الملخص EN
The static recrystallisation behaviour of a low carbon 3% Silicon steel, which is ferritic at high temperatures.
has been investigated using a single-pass hot rolling experiment.
The hot-rolling tests were carried out in a temperature of 900 "C to 9mm thickness followed by holding at the same temperature, using specimens of the two extruded bars.
With increasing rolling reduction and holding time after rolling, the fraction recrystallised increased.
The.
preferential area for this recrystallisation was the previous grain boundaries, particularly triple points of boundaries where the strain was concentrated.
In this fine grain size material, the possibility of consistent results needs better control of strain and temperature under the wedge shaped material
الملخص FRE
Le comportement de la recristallisation statique d'un acier à 3% de Silicium à bas carbone qui représente la phase ferritique à des températures élevées a été examiné en utilisant des essais de laminage à chaud à une seule passe.
Les essais de laminage à chaud étaient réalisés à une température de laminage de 9Q0°C jusqu'à uns épaisseur finale de 900mm, suivi par un maintien à la même température de laminage.
Le volume rccristallisé augmente avec l’augmentation de la réduction par laminage à chaud et le temps de maintien après laminage.
La zone privilégiée pour cette recristaiiisation était les joints des grains précédents, en particulier les points triples des joints ou la déformation était bien concentrée.
Dans ce matériau à taille de grain fine, la possibilité d’avoir des résultats compatibles lorsqu'en utilise un matériau qui la forme d’une cale, nécessite un contrôle dominant de la déformation et de la température de deformation.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Bin Shuayb, R.& Sellars, C. M.& Richardson, G. j.. 2003. Hot deformation behaviour of 3% silicon steel under wedge shaped specimens. Synthèse،Vol. 2003, no. 12, pp.25-32.
https://search.emarefa.net/detail/BIM-388708
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Bin Shuayb, R.…[et al.]. Hot deformation behaviour of 3% silicon steel under wedge shaped specimens. Synthèse No. 12 (Jun. 2003), pp.25-32.
https://search.emarefa.net/detail/BIM-388708
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Bin Shuayb, R.& Sellars, C. M.& Richardson, G. j.. Hot deformation behaviour of 3% silicon steel under wedge shaped specimens. Synthèse. 2003. Vol. 2003, no. 12, pp.25-32.
https://search.emarefa.net/detail/BIM-388708
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references : p. 31-32
رقم السجل
BIM-388708
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)