Morphology and In Vitro Behavior of Electrospun Fibrous Poly(D,L-lactic acid) for Biomedical Applications
المؤلفون المشاركون
Inami, Toshihiro
Shibata, Yo
Kasai, Kazutaka
Tanimoto, Yasuhiro
Ueda, Masayuki
Yamaguchi, Masaru
Hirayama, Satoshi
المصدر
Advances in Materials Science and Engineering
العدد
المجلد 2013، العدد 2013 (31 ديسمبر/كانون الأول 2013)، ص ص. 1-6، 6ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2013-05-27
دولة النشر
مصر
عدد الصفحات
6
التخصصات الرئيسية
العلوم الهندسية و تكنولوجيا المعلومات
الملخص EN
This work describes the fabrication, optimization, and characterization of electrospun fibrous poly(D,L-lactic acid) (PDLLA) for biomedical applications.
The influences of the polymer concentration of the electrospinning solution (5, 10, or 15 wt%) and the solution flow rate (0.1, 0.5, 1.0, or 2.0 mL/h) on the morphology of the obtained fibrous PDLLA were evaluated.
The in vitro biocompatibility of two types of PDLLA, ester terminated PDLLA (PDLLA-R) and carboxyl terminated PDLLA (PDLLA-COOH), was evaluated by monitoring apatite formation on samples immersed in Hanks’ balanced salt (HBS) solution.
15 wt% polymer solution was the most beneficial for preparing a fibrous PDLLA structure.
Meanwhile, no differences in morphology were observed for PDLLA prepared at various flow rates.
Apatite precipitate is formed on both types of PDLLA only 1 day after immersion in HBS solution.
After 7 days of immersion, PDLLA-COOH showed greater apatite formation ability compared with that of PDLLA-R, as measured by thin-film X-ray diffraction.
The results indicated that the carboxyl group is effective for apatite precipitation in the body environment.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Inami, Toshihiro& Tanimoto, Yasuhiro& Ueda, Masayuki& Shibata, Yo& Hirayama, Satoshi& Yamaguchi, Masaru…[et al.]. 2013. Morphology and In Vitro Behavior of Electrospun Fibrous Poly(D,L-lactic acid) for Biomedical Applications. Advances in Materials Science and Engineering،Vol. 2013, no. 2013, pp.1-6.
https://search.emarefa.net/detail/BIM-448965
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Inami, Toshihiro…[et al.]. Morphology and In Vitro Behavior of Electrospun Fibrous Poly(D,L-lactic acid) for Biomedical Applications. Advances in Materials Science and Engineering No. 2013 (2013), pp.1-6.
https://search.emarefa.net/detail/BIM-448965
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Inami, Toshihiro& Tanimoto, Yasuhiro& Ueda, Masayuki& Shibata, Yo& Hirayama, Satoshi& Yamaguchi, Masaru…[et al.]. Morphology and In Vitro Behavior of Electrospun Fibrous Poly(D,L-lactic acid) for Biomedical Applications. Advances in Materials Science and Engineering. 2013. Vol. 2013, no. 2013, pp.1-6.
https://search.emarefa.net/detail/BIM-448965
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-448965
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)