Mild Hydrothermal Synthesis of Ni–Cu Nanoparticles

الملخص EN

Magnetic Ni-rich Ni–Cu nanoparticles with Ni : Cu mass ratio (S) of 2.0 and 2.6 were prepared using a mixture of polyoxyethylene (10) isooctylphenyl ether (Triton X-100) and sodium dodecyl sulfate (SDS) in a mild hydrothermal condition at 95ºC.

X-ray diffractometry (XRD) showed that the nanoparticles prepared at S=2.0 possessed Ni–Cu alloy characteristic whereas the characteristic was absent at S=2.6.

The XRD data was enhanced by Fourier transform infrared spectroscopy (FTIR) which exhibited metal-metal (Ni–Cu) band at 455 cm−1.

Based on transmission electron microscopy (TEM), the average particle sizes for the nanoparticles prepared at S=2.0 and 2.6 were in the range of 19–23 nm.

The as-prepared nanoparticles exhibited paramagnetic behaviour measured using a vibrating sample magnetometer (VSM) and the specific saturation magnetization decreased at the higher concentration of Ni.