High-Efficiency 6′′ Multicrystalline Black Solar Cells Based on Metal-Nanoparticle-Assisted Chemical Etching

الملخص EN

Multicrystalline silicon (mc-Si) photovoltaic (PV) solar cells with nanoscale surface texturing by metal-nanoparticle-assisted etching are proposed to achieve high power efficiency.

The investigation of average nanorod lengths from 100 nm to 1 μm reveals that the Si wafer decorated with 100 nm thick nanorods has optical reflection of 9.5% inferior than the one with 1 μm thick nanorods (2%).

However, the short nanorods improve the doping uniformity and effectively decrease metal contact resistance.

After surface passivation using the hydrogenated SiO2/SiNx (5 nm/50 nm) stack, the minority carrier lifetime substantially increases from 1.8 to 7.2 μs for the 100 nm-thick nanorod solar cell to achieve the high power efficiency of 16.38%, compared with 1 μm thick nanorod solar cell with 11.87%.