Corrosion Inhibition Effect of 4-(2-Diethylamino-Ethylsulfonyl)‎-Phthalonitrile and 4,5-Bis(Hexylsulfonyl)‎-Phthalonitrile

الملخص EN

Inhibition of stainless steel corrosion in a 3.0 M NaCl solution by 4-(2-diethylamino-ethylsulfanyl)-phthalonitrile (DAESPN) and 4,5-bis(hexylsulfonyl)-phthalonitrile (Bis-HSPN) was investigated by polarization and electrochemical impedance spectroscopy (EIS) measurements.

The values of cathodic (βc) and anodic (βa) Tafel slopes, icorr, Ecorr, corrosion rate (CR), and inhibition efficiences (IE%) obtained from polarization curves and polarization resistance (RP), double-layer capacitance (Cdl), specific capacitance (Csp) values were obtained from EIS.

Double-layer capacitance differences in the presence and absence of inhibitors were also obtained from EIS measurements as suggested in the literature in order to investigate the interaction of them with metal surface.

Results show that both DAESPN and Bis-HSPN are effective in cathodic reaction.

Impedance measurements suggest higher surface coverage for DAESPN.

The interaction between the inhibitor and the stainless steel was investigated by the adsorption isotherm.

Langmuir adsorption isotherm Kads was applied and ΔG values were obtained and found as 4.32×10−4, 1.17×10−4 and 9.2 kJ, 12.5 kJ for DAESPN and Bis-HSPN, respectively, which suggests the electrostatic interaction between charged metal surface and charged organic molecules.