Role of Silicon Dioxide Filler on Mechanical and Dry Sliding Wear Behaviour of Glass-Epoxy Composites

الملخص EN

The mechanical properties and dry sliding wear behaviour of glass fabric reinforced epoxy (G-E) composite with varying weight percentage of silicon dioxide (SiO2) filler have been studied in the present work.

The influence of sliding distance, velocity, and applied normal load on dry sliding wear behaviour has been considered using Taguchi's L9 orthogonal array.

Addition of SiO2 increased the density, hardness, flexural, and impact strengths of G-E composite.

Results of dry sliding wear tests showed increasing wear volume with increase in sliding distance, load, and sliding velocity for G-E and SiO2 filled G-E composites.

Taguchi's results indicate that the sliding distance played a significant role followed by applied load, sliding velocity, and SiO2 loading.

Scanning electron micrographs of the worn surfaces of composite samples at different test parameters show smooth surface, microploughing, and fine grooves under low load and velocity.

However, severe damage of matrix with debonding and fiber breakage was seen at high load and velocity especially in unfilled G-E composite.