Enhanced Photocatalytic Degradation of Methylene Blue Using ZnFe2O4MWCNT Composite Synthesized by Hydrothermal Method

الملخص EN

Multiwalled carbon nanotubes (MWCNTs) were synthesized using arc discharge method at a magnetic field of 430 G and purified using HNO3/H2O2.

Transmission electron micrographs revealed that MWCNTs had inner and outer diameter of ~2 nm and ~4 nm, respectively.

Raman spectroscopy confirmed formation of MWCNTs showing G-band at 1577 cm−1.

ZnFe2O4 and ZnFe2O4/MWCNT were produced using one step hydrothermal method.

Powder X-ray diffraction (XRD) confirmed the formation of cubic spinel ZnFe2O4 as well as incorporation of MWCNT into ZnFe2O4.

Visible light photocatalytic degradation of methylene blue (MB) was studied using pure ZnFe2O4 and ZnFe2O4/MWCNT.

The results showed that ZnFe2O4/MWCNT composite had higher photocatalytic activity as compared to pure ZnFe2O4.

After irradiation for 5 hours in the visible light, MB was almost 84% degraded in the presence of ZnFe2O4 photocatalyst, while 99% degradation was observed in case of ZnFe2O4/MWCNT composite.

This enhancement in the photocatalytic activity of composite may be attributed to the inhibition of recombination of photogenerated charge carriers.