Environmental and Material Influences on the Stress-Corrosion Cracking of Steel in H2O–CO–CO2 Solutions
المؤلف
المصدر
International Journal of Corrosion
العدد
المجلد 2012، العدد 2012 (31 ديسمبر/كانون الأول 2012)، ص ص. 1-13، 13ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2012-07-08
دولة النشر
مصر
عدد الصفحات
13
التخصصات الرئيسية
الملخص EN
The stress-corrosion cracking of A516 pressure vessel steel was investigated by the use of slow strain-rate tests.
The orientation of samples to the rolling direction was investigated, and it was found that samples machined longitudinal to the rolling direction showed a slightly increased sensitivity to stress corrosion.
The temperature variation showed that for different gas mixtures, the maximum sensitivity to stress corrosion was in the region of 45° to 55°C for the 25% CO gas mixture, whereas with higher CO concentrations, this temperature region of maximum sensitivity moved to higher temperatures.
Surface finish showed a slight increase in sensitivity to cracking with increased surface roughness.
The most significant increase was found with increased total gas pressures and when samples have been exposed to the environment for an extended period.
This was as a result of the inhibition of the corrosion reaction by the passivation of the carbon monoxide, which is a time-dependent process.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
van der Merwe, J. W.. 2012. Environmental and Material Influences on the Stress-Corrosion Cracking of Steel in H2O–CO–CO2 Solutions. International Journal of Corrosion،Vol. 2012, no. 2012, pp.1-13.
https://search.emarefa.net/detail/BIM-470246
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
van der Merwe, J. W.. Environmental and Material Influences on the Stress-Corrosion Cracking of Steel in H2O–CO–CO2 Solutions. International Journal of Corrosion No. 2012 (2012), pp.1-13.
https://search.emarefa.net/detail/BIM-470246
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
van der Merwe, J. W.. Environmental and Material Influences on the Stress-Corrosion Cracking of Steel in H2O–CO–CO2 Solutions. International Journal of Corrosion. 2012. Vol. 2012, no. 2012, pp.1-13.
https://search.emarefa.net/detail/BIM-470246
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-470246
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)