Synthesis and Performance of an Acrylamide Copolymer Containing Nano-SiO2 as Enhanced Oil Recovery Chemical

الملخص EN

A novel copolymer containing nano-SiO2 was synthesized by free radical polymerization using acrylamide (AM), acrylic acid (AA), and nano-SiO2 functional monomer (NSFM) as raw materials under mild conditions.

The AM/AA/NSFM copolymer was characterized by infrared (IR) spectroscopy, 1H NMR spectroscopy, elemental analysis, and scanning electron microscope (SEM).

It was found that the AM/AA/NSFM copolymer exhibited higher viscosity than the AM/AA copolymer at 500 s−1 shear rate (18.6 mPa·s versus 8.7 mPa·s).

It was also found that AM/AA/NSFM could achieve up to 43.7% viscosity retention rate at 95°C.

Mobility control results indicated that AM/AA/NSFM could establish much higher resistance factor (RF) and residual resistance factor (RRF) than AM/AA under the same conditions (RF: 16.52 versus 12.17, RRF: 3.63 versus 2.59).

At last, the enhanced oil recovery (EOR) of AM/AA/NSFM was up to 20.10% by core flooding experiments at 65°C.