Multiscale Hybrid Micro-Nanocomposites Based on Carbon Nanotubes and Carbon Fibers

الملخص EN

Amino-modified double wall carbon nanotube (DWCNT-NH2)/carbon fiber (CF)/epoxy hybrid micro-nanocomposite laminates were prepared by a resin infusion technique.

DWCNT-NH2/epoxy nanocomposites and carbon fiber/epoxy microcomposites were made for comparison.

Morphological analysis of the hybrid composites was performed using field emission scanning electron microscope.

A good dispersion at low loadings of carbon nanotubes (CNTs) in epoxy matrix was achieved by a bath ultrasonication method.

Mechanical characterization of the hybrid micro-nanocomposites manufactured by a resin infusion process included three-point bending, mode I interlaminar toughness, dynamic mechanical analysis, and drop-weight impact testing.

The addition of small amounts of CNTs (0.025, 0.05, and 0.1 wt%) to epoxy resins for the fabrication of multiscale carbon fiber composites resulted in a maximum enhancement in flexural modulus by 35%, a 5% improvement in flexural strength, a 6% improvement in absorbed impact energy, and 23% decrease in the mode I interlaminar toughness.

Hybridization of carbon fiber-reinforced epoxy using CNTs resulted in a reduction in Tg and dampening characteristics, presumably as a result of the presence of micron-sized agglomerates.