OxidationCorrosion Behaviour of ODS FerriticMartensitic Steels in Pb Melt at Elevated Temperature

الملخص EN

Lead-based melts (Pb, Pb-Bi) are considered as candidate coolants and spallation neutron targets due to their excellent thermophysical and nuclear properties.

However, the corrosion of structural materials remains a major issue.

Oxide dispersion strengthened (ODS) ferritic/martensitic steels are considered for high temperature application for both fission and fusion reactor concepts.

The oxidation/corrosion kinetics in a static oxygen-saturated Pb melt at temperature of 550°C as well as the morphology and composition of scales formed on ferritic/martensitic Fe-9Cr-1.5W and ferritic Fe-14Cr-1.5W ODS steels have been investigated.

Both materials showed homogeneous multiple, dense scales that consisted of typical combination of Fe3O4 as outer sublayer and (Fe,Cr)3O4 as inner sublayer.

A nonuniform growth of inner oxide sublayers into the metal matrix as well as a good adhesion to the metal substrate is observed.

With the prolongation of exposure from 240 to 1000 h, observed scales grow from 35 µm to 45 µm for ODS Fe-9Cr steel and from 40 µm to 60 µm for ODS Fe-14Cr steel with the thinning rates of 0,22 and 0,31 mm/year correspondingly.

The mechanism of scales formation is discussed.