Synthesis and Characterization of Gold Nanoparticles with Plasmon Absorbance Wavelength Tunable from Visible to Near Infrared Region

الملخص EN

Gold nanorods with localized surface plasmon resonance (LSPR) can be chemically synthesized.

We systematically investigated the effects of reaction parameters and centrifugation on the fine tuning of the rod dimension in scale-up production (80–100 mL).

Nanorods of absorption bands from 600–1050 nm were fabricated with precise control of the aspect ratio (AR) from 1.5 to 8.9.

Although all chemicals are important in directing the nanostructure, silver ion concentration and seed/Au3+ ratio were the most effective variations to adjust the absorption wavelength.

With a single surfactant under the influence of silver nitrate, short nanorods up to AR of 5 were synthesized with corresponding maximum absorption wavelength at 902 nm.

To achieve higher aspect ratio with absorption band beyond 1,000 nm, two-surfactant growth solution was sought to further elongate the rod length.

Centrifugation speed and times were found to exert significant influences on the final rod dimension, which is important during the purification process.

In a relatively large quantity nanorod synthesis, even distribution and sufficient mixing of chemical ingredients play an essential role in determining the yield, uniformity, and stability of the final nanorod formation.