Deposition of Cerium-Based Conversion Coatings on Aluminum Alloy 380
المؤلفون المشاركون
Maddela, Surender
O'Keefe, Matthew J.
Lin, Ci
Fahrenholtz, William G.
المصدر
International Journal of Corrosion
العدد
المجلد 2012، العدد 2012 (31 ديسمبر/كانون الأول 2012)، ص ص. 1-9، 9ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2012-09-11
دولة النشر
مصر
عدد الصفحات
9
التخصصات الرئيسية
الملخص EN
Cerium-based conversion coatings were deposited on as-cast aluminum alloy 380 substrates by a spontaneous immersion process.
In this study, the effects of rinsing temperature prior to immersion in the coating deposition solution were studied with respect to the surface morphology, electrochemical response, and corrosion resistance of the coatings.
Panels rinsed at 25°C prior to coating had large cracks and holes in the coating.
In contrast, panels rinsed at 100°C prior to coating had a uniform coating morphology with fewer, smaller cracks.
Electrochemical testing revealed that coatings deposited on substrates rinsed at 100°C had higher impedance (~80 kΩ·cm2) and lower corrosion current (~0.34 μA/cm2) compared to coatings deposited on substrates rinsed at 25°C, which had 10 kΩ·cm2 impedance and 2.7 μA/cm2 corrosion current.
Finally, ASTM B117 salt spray testing showed that rinsing at 100°C prior to coating resulted in cerium-based conversion coatings that could resist the formation of salt tails for at least 8 days.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Lin, Ci& Maddela, Surender& Fahrenholtz, William G.& O'Keefe, Matthew J.. 2012. Deposition of Cerium-Based Conversion Coatings on Aluminum Alloy 380. International Journal of Corrosion،Vol. 2012, no. 2012, pp.1-9.
https://search.emarefa.net/detail/BIM-496589
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Lin, Ci…[et al.]. Deposition of Cerium-Based Conversion Coatings on Aluminum Alloy 380. International Journal of Corrosion No. 2012 (2012), pp.1-9.
https://search.emarefa.net/detail/BIM-496589
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Lin, Ci& Maddela, Surender& Fahrenholtz, William G.& O'Keefe, Matthew J.. Deposition of Cerium-Based Conversion Coatings on Aluminum Alloy 380. International Journal of Corrosion. 2012. Vol. 2012, no. 2012, pp.1-9.
https://search.emarefa.net/detail/BIM-496589
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-496589
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)