Parameters Controlling the Oxide Reduction during Sintering of Chromium Prealloyed Steel
المؤلفون المشاركون
Hryha, Eduard
Dudrová, Eva
Hrubovčáková, Monika
Kabátová, Margita
Harvanová, Jarmila
المصدر
Advances in Materials Science and Engineering
العدد
المجلد 2013، العدد 2013 (31 ديسمبر/كانون الأول 2013)، ص ص. 1-16، 16ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2013-10-09
دولة النشر
مصر
عدد الصفحات
16
التخصصات الرئيسية
العلوم الهندسية و تكنولوجيا المعلومات
الملخص EN
Temperature intervals of oxide reduction processes during sintering of the Fe-3%Cr-0.5%Mo prealloyed powder using continuous monitoring of processing-exhaust gas composition (CO, CO2, and H2O) were identified and interpreted in relation to density (6.5–7.4 g/cm3), sintering temperature (1120 and 1200°C), heating and cooling rates (10 and 50°C/min), carbon addition (0.5/0.6/0.8%), type (10%H2-N2, N2), and purity (5.0 and 6.0) of the sintering atmosphere.
The progress in reduction processes was evaluated by oxygen and carbon contents in sintered material and fracture strength values as well.
Higher sintering temperature (1200°C) and density <7.0 g/cm3 resulted in a relative decrease of oxygen content by more than 80%.
The deterioration of microclimate purity of inner microvolumes of compacts shifted the thermodynamic equilibrium towards oxidation.
It resulted in a closing of residual oxides inside interparticle necks.
The reducing ability of the N2 atmosphere can be improved by sintering in a graphite container.
High density of 7.4 g/cm3 achieved by double pressing indicated a negative effect on reduction processes due to restricted replenishment of the microclimate atmosphere with the processing gas.
In terms of strength properties, carbon content should not be higher than ~0.45%.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Hrubovčáková, Monika& Dudrová, Eva& Hryha, Eduard& Kabátová, Margita& Harvanová, Jarmila. 2013. Parameters Controlling the Oxide Reduction during Sintering of Chromium Prealloyed Steel. Advances in Materials Science and Engineering،Vol. 2013, no. 2013, pp.1-16.
https://search.emarefa.net/detail/BIM-498184
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Hrubovčáková, Monika…[et al.]. Parameters Controlling the Oxide Reduction during Sintering of Chromium Prealloyed Steel. Advances in Materials Science and Engineering No. 2013 (2013), pp.1-16.
https://search.emarefa.net/detail/BIM-498184
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Hrubovčáková, Monika& Dudrová, Eva& Hryha, Eduard& Kabátová, Margita& Harvanová, Jarmila. Parameters Controlling the Oxide Reduction during Sintering of Chromium Prealloyed Steel. Advances in Materials Science and Engineering. 2013. Vol. 2013, no. 2013, pp.1-16.
https://search.emarefa.net/detail/BIM-498184
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-498184
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر