Mesoporous TiO2 Micro-Nanometer Composite Structure : Synthesis, Optoelectric Properties, and Photocatalytic Selectivity

الملخص EN

Mesoporous anatase TiO2 micro-nanometer composite structure was synthesized by solvothermal method at 180°C, followed by calcination at 400°C for 2 h.

The as-prepared TiO2 was characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), and Fourier transform infrared spectrum (FT-IR).

The specific surface area and pore size distribution were obtained from N2 adsorption-desorption isotherm, and the optoelectric property of the mesoporous TiO2 was studied by UV-Vis absorption spectrum and surface photovoltage spectra (SPS).

The photocatalytic activity was evaluated by photodegradation of sole rhodamine B (RhB) and sole phenol aqueous solutions under simulated sunlight irradiation and compared with that of Degussa P-25 (P25) under the same conditions.

The photodegradation preference of this mesoporous TiO2 was also investigated for an RhB-phenol mixed solution.

The results show that the TiO2 composite structure consists of microspheres (∼0.5–2 μm in diameter) and irregular aggregates (several hundred nanometers) with rough surfaces and the average primary particle size is 10.2 nm.

The photodegradation activities of this mesoporous TiO2 on both RhB and phenol solutions are higher than those of P25.

Moreover, this as-prepared TiO2 exhibits photodegradation preference on RhB in the RhB-phenol mixture solution.