Chemical Phase Separation of Superconductive and Ferromagnetic Domains in ZnNNi3−xCox

الملخص EN

Various ZnNyNi3−xCox compounds with differing Co content, x, were synthesized, and their magnetic properties were investigated.

Uniform solid solutions could not be obtained at low Co content (x<0.75); instead micrometer-scaled ferromagnetic ZnNyNi0.6Co2.4 domains formed embedded within a superconductive ZnNNi3 bulk, showing chemical phase separation of superconductive ZnNNi3 and ferromagnetic ZnNyNi0.6Co2.4.

At intermediate levels of Co concentration (0.75

Only at high Co concentration (x>2) the uniform ferromagnetic solid solution ZnNyNi3−xCox (with most likely y=0.5) formed.

The phase separation behavior is intrinsic to the system, reflecting the existence of a miscibility gap in ZnNyNi3−xCox for the samples with x<2, and was shown not to be attributable to incomplete synthesis.

In the two-phased samples, high-quality granular contact between the superconductor and ferromagnet has been realized, suggesting that the production of useful devices requiring high-quality contacts between superconductors and ferromagnets may be possible by making use of this two-phase situation.