Surface and Core Electronic Structure of Oxidized Silicon Nanocrystals

الملخص EN

Ab initio restricted Hartree-Fock method within the framework of large unit cell formalism is used to simulate silicon nanocrystals between 216 and 1000 atoms (1.6–2.65 nm in diameter) that include Bravais and primitive cell multiples.

The investigated properties include core and oxidized surface properties.

Results revealed that electronic properties converge to some limit as the size of the nanocrystal increases.

Increasing the size of the core of a nanocrystal resulted in an increase of the energy gap, valence band width, and cohesive energy.

The lattice constant of the core and oxidized surface parts shows a decreasing trend as the nanocrystal increases in a size that converges to 5.28 Ǻ in a good agreement with the experiment.

Surface and core convergence to the same lattice constant reflects good adherence of oxide layer at the surface.

The core density of states shows highly degenerate states that split at the oxygenated (001)-(1×1) surface due to symmetry breaking.

The nanocrystal surface shows smaller gap and higher valence and conduction bands when compared to the core part, due to oxygen surface atoms and reduced structural symmetry.

The smaller surface energy gap shows that energy gap of the nanocrystal is controlled by the surface part.

Unlike the core part, the surface part shows a descending energy gap that proves its obedience to quantum confinement effects.

Nanocrystal geometry proved to have some influence on all electronic properties including the energy gap.