دراسة تأثير التعويض الجزئي و التلدين المتكرر في الخصائص الكهربائية للمركب Tl2-xAgxSr2-yBayCa2Cu3O10+δ الفائق التوصيل الكهربائي المحضر بتقنية النانو

الملخص EN

The crystal compounds Tl2-xAg2-ySryBayCa2Cu3O10+& are successfully prepared in different concentrations (x, y = 0.1, 0.2, 0.3, 0.4, 0.5) by solid state reaction process.

The samples were then subjected to Nano technique under hydrolic pressure 8 ton/cm2.

samples have been annealed in (850 C0) for 72 hours.

The results show a best value at x, y = 0.3 ratio of Ag, Ba.

Electrical resistivity at x, y = 0.3 of Ag, Ba are obtained when the best value of Tc = 141 K.

Samples morphology were also observed by AFM (in three dimensions), the best value of Nano is 91.74 nm at x, y = 0.3.

Morphological structures of the surface were also observed by (SEM) and (EDX) show that there are dark regions and light which indicate the presence of heavy elements and light elements on the installation.