Synthesis of mullite powder from aluminum nitrate and precipitated silica using sol-gel process
المؤلف
المصدر
Engineering and Technology Journal
العدد
المجلد 34، العدد 8A (31 أغسطس/آب 2016)، ص ص. 1491-1498، 8ص.
الناشر
تاريخ النشر
2016-08-31
دولة النشر
العراق
عدد الصفحات
8
التخصصات الرئيسية
العلوم الهندسية والتكنولوجية (متداخلة التخصصات)
الملخص EN
In this work, a new route for possibility synthesizing high purity submicron size mullite (3A12O3.2SiO2) powder at relatively low temperature.
Mullite precursor has been prepared from mixing precipitated silica powder with solution of aluminum nitrate nonahydrate (Al(NO3)3.9H2O) through sol-gel process, in order to obtain composite powder.
The formed precursor gel was calcined at temperatures of (1100, 1150, 1200 and 1250)°C for 1 hour.
The influence of calcination temperatures of the mullite synthesis was discussed.
The microstructure tests of calcined materials were investigated by x-ray diffractometer (XRD), scanning electron microscopy (SEM), and energy dispersive x-ray spectroscopy (EDX).
X-ray analysis results identified the mullitization initiated at 1200°C, and the mullite phase was completely formed at 1250°C.
The SEM micrographs show the microstructure of mullite powder had been aggregated in the regular and nearly spherical-like appearances with diameters in the range of (100-200) nm.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Jabir, Husayn Ala. 2016. Synthesis of mullite powder from aluminum nitrate and precipitated silica using sol-gel process. Engineering and Technology Journal،Vol. 34, no. 8A, pp.1491-1498.
https://search.emarefa.net/detail/BIM-706720
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Jabir, Husayn Ala. Synthesis of mullite powder from aluminum nitrate and precipitated silica using sol-gel process. Engineering and Technology Journal Vol. 34, no. 8A (Aug. 2016), pp.1491-1498.
https://search.emarefa.net/detail/BIM-706720
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Jabir, Husayn Ala. Synthesis of mullite powder from aluminum nitrate and precipitated silica using sol-gel process. Engineering and Technology Journal. 2016. Vol. 34, no. 8A, pp.1491-1498.
https://search.emarefa.net/detail/BIM-706720
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references : p. 1497-1498
رقم السجل
BIM-706720
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)