Effect of Sb2O3 and or CdO nanoparticle substitution on the properties of high-TC superconducting Bi1.6-x SbxPb0.4Sr2Ca2yCdyCu3OZ material
العناوين الأخرى
تأثير الاستبدال الجيزيئي بالدقائق الثانوية Cd2O3 و أو Sb2O3 على خواص المادة الفائقة التوصيلية Bi1.6-x SbxPb0.4Sr2Ca2-yCdyCu3OZ
المؤلف
المصدر
العدد
المجلد 16، العدد 36 (30 إبريل/نيسان 2018)، ص ص. 73-84، 12ص.
الناشر
تاريخ النشر
2018-04-30
دولة النشر
العراق
عدد الصفحات
12
التخصصات الرئيسية
الملخص EN
High temperature superconductors materials with composition Bi1.6-xSbxPb0.4Sr2Ca2-yCdyCu3OZ (x = 0, 0.1, 0.2 and 0.3) and (y = 0.01 and 0.02), were prepared by using the chemical reaction in solid-state ways, and test influence of partial replacement of Bi and Ca with Sb and Cd respectively on the superconducting properties, all samples were sintered at the same temperature (850 oC) and for the same time (195 h).
The structural analysis of the prepared samples was carried out using X-ray diffraction (XRD) measurements performed at room temperature, scanning electron microscope (SEM) and dc electrical resistivity was measured as a function of temperature.
It was found that the sample prepared by partial substitution of Sb at ratio (x= 0.2) and Cd with ratio (y=0.01), has the maximum value of zero resistance temperature, where was the TC(onset) and TC(0) values for this sample are (140 K) and (123 K) respectively, and XRD results reveal that this sample has the highest percentage of Bi- 2223 phase, as well as the analysis of XRD patterns of the prepared materials showed polycrystalline structure and signalize that all samples had an orthorhombic crystalline structure.
It was concluded that Sb2O3 nanoparticles it may be acts as a flux agent in the matrix to lower the partial melting temperature of the samples and that leads to the promotion of the high-TC phase.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
al-Shaliji, Sihama Isa Salih. 2018. Effect of Sb2O3 and or CdO nanoparticle substitution on the properties of high-TC superconducting Bi1.6-x SbxPb0.4Sr2Ca2yCdyCu3OZ material. Iraqi Journal of Physics،Vol. 16, no. 36, pp.73-84.
https://search.emarefa.net/detail/BIM-835526
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
al-Shaliji, Sihama Isa Salih. Effect of Sb2O3 and or CdO nanoparticle substitution on the properties of high-TC superconducting Bi1.6-x SbxPb0.4Sr2Ca2yCdyCu3OZ material. Iraqi Journal of Physics Vol. 16, no. 36 (Apr. 2018), pp.73-84.
https://search.emarefa.net/detail/BIM-835526
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
al-Shaliji, Sihama Isa Salih. Effect of Sb2O3 and or CdO nanoparticle substitution on the properties of high-TC superconducting Bi1.6-x SbxPb0.4Sr2Ca2yCdyCu3OZ material. Iraqi Journal of Physics. 2018. Vol. 16, no. 36, pp.73-84.
https://search.emarefa.net/detail/BIM-835526
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references : p. 83-84
رقم السجل
BIM-835526
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)