Microstructure and phases analysis for advanced plasma sprayed zirconia-ceria-yttria thermal barrier coating

الملخص EN

Thoroughly qualitative and quantitative topography, microstructure, splats formation and phases evaluation were made to understand carefully the behavior of plasma sprayed zirconia-ceria-yttria coatings processed under near optimum processing conditions.

The study is focused on how to design and select the given property to predict the reliable data of plasma sprayed zirconia-20 wt% CeO2-3.6 wt% Y2O3.

The processing and plasma spraying parameters were designed carefully to give a reliable clear evaluation of the microstructure.

The results showed a heterogeneous microstructure in which melted, semimelted and unmelted particles were existed.

The phases formed are consisted of nontranformable tetragonal phase (t') with small amount (less than 2 mole%) of monoclinic phase (m).

The electron probe microanalysis (EPMA) suggests the intimate mixing between the binary systems of zirconia-ceria and zirconia-yttria during spraying.

The Image J technique, SEM, EPMA, EDS and XRD/step scan XRD were used collectively to build up a clear picture on the solidification mechanism of the new plasma sprayed coating system.