Study of fatigue fractography of mild steel used in automotiv industry
العناوين الأخرى
دراسة مقطع كسر الكلال للفولاذ المطاوع المستخدم في صناعة السيارات
المؤلف
المصدر
al-Khwarizmi Engineering Journal
العدد
المجلد 15، العدد 1 (31 مارس/آذار 2019)، ص ص. 82-88، 7ص.
الناشر
جامعة بغداد كلية هندسة الخوارزمي
تاريخ النشر
2019-03-31
دولة النشر
العراق
عدد الصفحات
7
التخصصات الرئيسية
الموضوعات
الملخص EN
Fatigue failure is almost considered as the predominant problem affecting automotive parts under dynamic loading condition.
Thus, more understanding of crack behavior during fatigue can strongly help in finding the proper mechanism to avoid the final fracture and extent the service life of components.
The main goal of this paper is to study the fracture behavior of low carbon steel which is used mostly in automotive industry.
For this purpose, the fractography of samples subjected to high and low stress levels in fatigue test then was evaluated and analyzed.
Hardness and tensile tests were carried out to determine the properties of used steel.
Also, the samples were characterized by microstructure test and XRD analysis to examine the constitute phases.
The fatigue test (S-N curve) was done at stress ratio (R= -1), and the fracture examination was perform using Scanning Electron Microscope (SEM).
The results of microstructure and XRD analysis were indicating that the Ferrite and a little amount of pearlite are the dominant phases of this steel.
Whereas, the fractography observations reveal that the void coalescence ductile fracture is the main failure mode in samples with high stress level, while the ductile fracture (void coalescence) with Transgranular Cleavage fracture was noticed in low stress fatigue mode for this alloy.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Zayn al-Abidin, Ahmad Amid. 2019. Study of fatigue fractography of mild steel used in automotiv industry. al-Khwarizmi Engineering Journal،Vol. 15, no. 1, pp.82-88.
https://search.emarefa.net/detail/BIM-893086
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Zayn al-Abidin, Ahmad Amid. Study of fatigue fractography of mild steel used in automotiv industry. al-Khwarizmi Engineering Journal Vol. 15, no. 1 (Mar. 2019), pp.82-88.
https://search.emarefa.net/detail/BIM-893086
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Zayn al-Abidin, Ahmad Amid. Study of fatigue fractography of mild steel used in automotiv industry. al-Khwarizmi Engineering Journal. 2019. Vol. 15, no. 1, pp.82-88.
https://search.emarefa.net/detail/BIM-893086
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references : p. 86-87
رقم السجل
BIM-893086
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)