The influence of graphite content and milling time on hardness, compressive strength and wear volume of copper-graphite composites prepared via powder metallurgy
العناوين الأخرى
تأثير محتوى الكرافيت و زمن الطحن على الصلادة، مقاومة الانضغاط، حجم البلى لمتراكبات النحاس-كرافيت المحضرة بواسطة ميتالورجيا المساحيق
المؤلفون المشاركون
Mahdi, Faruq Mansur
Razzuqi, Raid Najib
Arhayyim, Sayf Sabah
المصدر
Tikrit Journal of Engineering Sciences
العدد
المجلد 24، العدد 3 (30 سبتمبر/أيلول 2017)، ص ص. 47-54، 8ص.
الناشر
تاريخ النشر
2017-09-30
دولة النشر
العراق
عدد الصفحات
8
التخصصات الرئيسية
الملخص EN
Copper – graphite composites are widely used in sliding bearings and brushes due to their excellent thermal and electrical conductivities and high wear resistance.
The aim of this research is to study the Influence of graphite content and milling time on hardness, compressive strength, wear volume and friction coefficient of copper - graphite composites prepared via powder metallurgy.
A powder mixture containing 0,5,10,15,20 and 25 vol% graphite was milled for 1,3,5,7 and 9 hours.
The milled mixture was cold pressed at 700 MPa for 30 second, followed by sintering at 900 oC for one hour.
It was found through this work that increasing milling time results an appreciate increase in hardness and radial compressive strength, slight reduction in wear volume and slight increase in the coefficient of friction for all compositions except that for pure copper in which a considerable increase in wear volume and decrease in the coefficient of friction was observed.
On the other hand, increasing the graphite volume fraction increases the composite hardness, till an optimum value, and decreases the radial compressive strength.
A great decrease in both wear volume and coefficient of friction was observed on increasing graphite content up to 25 vol%.
Finally, a graphite, cast iron chips and fireclay sintering configuration was found to be an effective procedure which minimize oxidation to levels comparative with those observed previously by sintering in argon or hydrogen atmospheres.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Mahdi, Faruq Mansur& Razzuqi, Raid Najib& Arhayyim, Sayf Sabah. 2017. The influence of graphite content and milling time on hardness, compressive strength and wear volume of copper-graphite composites prepared via powder metallurgy. Tikrit Journal of Engineering Sciences،Vol. 24, no. 3, pp.47-54.
https://search.emarefa.net/detail/BIM-946139
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Mahdi, Faruq Mansur…[et al.]. The influence of graphite content and milling time on hardness, compressive strength and wear volume of copper-graphite composites prepared via powder metallurgy. Tikrit Journal of Engineering Sciences Vol. 24, no. 3 (2017), pp.47-54.
https://search.emarefa.net/detail/BIM-946139
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Mahdi, Faruq Mansur& Razzuqi, Raid Najib& Arhayyim, Sayf Sabah. The influence of graphite content and milling time on hardness, compressive strength and wear volume of copper-graphite composites prepared via powder metallurgy. Tikrit Journal of Engineering Sciences. 2017. Vol. 24, no. 3, pp.47-54.
https://search.emarefa.net/detail/BIM-946139
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
رقم السجل
BIM-946139
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر