Development of surface roughness and mechanical properties of PMMA nanocomposites by blending with polymeric materials

الملخص EN

This work aims to a development of mechanical properties of PMMA that is utilized in denture material, by using two types of polymers; blends (PMMA:2%NR) and (PMMA:2%SR) as a matrix materials strengthen with natural nanoparticles from the pomegranate peel powder (PPP) that were added at different weight fractions (0.0, 0.1%, 0.3%, 0.5% and 0.7%).

Two groups of bio nanocomposites specimens were prepared, using (Hand Lay-Up) method.

Experimental tests were carried out on surface roughness, hardness and wear rate as well as analyzing of FTIR test.

The minimum values of surface roughness and wear rate were reached 1.51 nm and 0.317×10-8 g/cm respectively for polymer blend nanocomposite ((PMMA:2%NR): 0.7% PPP).

Whereas, the maximum value of Shore D hardness reached 90 for the same sample of nanocomposites.

According to these results, it can be a concluded that the addition of Nano pomegranate powder and natural rubber can develop the mechanical properties of PMMA material used in medical applications.