Cyclic Deformation Behavior and Fatigue Crack Propagation of Low Carbon Steel Prestrained in Tension
المؤلفون المشاركون
Jia, W. P.
Ju, D. Y.
Wang, J. G.
المصدر
Advances in Materials Science and Engineering
العدد
المجلد 2009، العدد 2009 (31 ديسمبر/كانون الأول 2009)، ص ص. 1-4، 4ص.
الناشر
Hindawi Publishing Corporation
تاريخ النشر
2009-06-08
دولة النشر
مصر
عدد الصفحات
4
الملخص EN
The tests were performed on low carbon steel plate.
In the tension fatigue tests, two angle values (ϕ=0° and ϕ=45°, ϕ is the angle between the loading and the rolling direction) have been chosen.
The influence of strain path change on the subsequent initial work softening rate and the saturation stress has been investigated.
Dislocation microstructure was observed by transmission electron microscopy.
It was found that the strain amount of preloading in tension has obviously affected the cyclic softening phenomenon and the initial cyclic softening rate.
It was observed that the reloading axial stress for ϕ=45° case increased more than that of ϕ=0° case, due to the anisotropism of Q235.
In the fatigue crack propagation tests, the experimental results show that with increasing the pretension deformation degree, the fatigue crack growth rate increases, especially at the near threshold section.
نمط استشهاد جمعية علماء النفس الأمريكية (APA)
Wang, J. G.& Jia, W. P.& Ju, D. Y.. 2009. Cyclic Deformation Behavior and Fatigue Crack Propagation of Low Carbon Steel Prestrained in Tension. Advances in Materials Science and Engineering،Vol. 2009, no. 2009, pp.1-4.
https://search.emarefa.net/detail/BIM-988294
نمط استشهاد الجمعية الأمريكية للغات الحديثة (MLA)
Wang, J. G.…[et al.]. Cyclic Deformation Behavior and Fatigue Crack Propagation of Low Carbon Steel Prestrained in Tension. Advances in Materials Science and Engineering No. 2009 (2009), pp.1-4.
https://search.emarefa.net/detail/BIM-988294
نمط استشهاد الجمعية الطبية الأمريكية (AMA)
Wang, J. G.& Jia, W. P.& Ju, D. Y.. Cyclic Deformation Behavior and Fatigue Crack Propagation of Low Carbon Steel Prestrained in Tension. Advances in Materials Science and Engineering. 2009. Vol. 2009, no. 2009, pp.1-4.
https://search.emarefa.net/detail/BIM-988294
نوع البيانات
مقالات
لغة النص
الإنجليزية
الملاحظات
Includes bibliographical references
رقم السجل
BIM-988294
قاعدة معامل التأثير والاستشهادات المرجعية العربي "ارسيف Arcif"
أضخم قاعدة بيانات عربية للاستشهادات المرجعية للمجلات العلمية المحكمة الصادرة في العالم العربي
![](/images/ebook-kashef.png)
تقوم هذه الخدمة بالتحقق من التشابه أو الانتحال في الأبحاث والمقالات العلمية والأطروحات الجامعية والكتب والأبحاث باللغة العربية، وتحديد درجة التشابه أو أصالة الأعمال البحثية وحماية ملكيتها الفكرية. تعرف اكثر
![](/images/kashef-image.png)