SiO 2 Antireflection Coatings Fabricated by Electron-Beam Evaporation for Black Monocrystalline Silicon Solar Cells

Abstract EN

In this work we prepared double-layer antireflection coatings (DARC) by using the SiO2/SiN x:H heterostructure design.

SiO2 thin films were deposited by electron-beam evaporation on the conventional solar cell with SiN x:H single-layer antireflection coatings (SARC), while to avoid the coverage of SiO2 on the front side busbars, a steel mask was utilized as the shelter.

The thickness of the SiN x:H as bottom layer was fixed at 80 nm, and the varied thicknesses of the SiO2 as top layer were 105 nm and 122 nm.

The results show that the SiO2/SiN x:H DARC have a much lower reflectance and higher external quantum efficiency (EQE) in short wavelengths compared with the SiN x:H SARC.

A higher energy conversion efficiency of 17.80% was obtained for solar cells with SiO2 (105 nm)/SiN x:H (80 nm) DARC, an absolute conversion efficiency increase of 0.32% compared with the conventional single SiN x:H-coated cells.