In Vitro Effects of Two Topical Varnish Materials and Er:YAG Laser Irradiation on Enamel Demineralization around Orthodontic Brackets

Abstract EN

The aim of this in vitro was to evaluate the effects of tricalcium phosphate (TCP) and amorphous calcium phosphate (ACP) containing varnish materials and Er:YAG laser irradiation on enamel demineralization around orthodontic brackets.

Forty extracted human premolar teeth were randomly divided into four treatment groups (i.e., 10 in each group): (1) 5% NaF-ACP varnish, (2) 5% NaF-TCP varnish, (3) Er:YAG laser, and (4) control (no treatment).

Er:YAG laser was operated at a wavelength of 2.94 μm and the energy output was 80 mJ per pulse; a pulse duration of 200 μsec and and a frequency of 2 Hz were used with water cooling.

All samples were then put into pH cycles.

Surface microhardness values and representative SEM images were assessed.

Surface microhardness values were evaluated using Kruskal-Wallis and Mann-Whitney U tests.

The results revealed that demineralization was significantly lower in the TCP and ACP varnish groups, whereas mean surface microhardness values of the TCP varnish were found higher than the ACP (P<0.05).

TCP and ACP varnish materials were found effective for reducing enamel demineralization around orthodontic brackets.

Use of Er:YAG laser irradiation as described in this study for inhibition of demineralization was found not satisfactory.