Investigation of Poly(3,4-ethylenedioxythiophene)‎:Poly(styrenesulfonate)‎ Hole Transport Layer for Solution-Processed Polymer Solar Cells

Abstract EN

The inverted polymer solar cell was prepared by self-made spray-coating system, and the poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) hole transport layer was studied.

220 nm poly-(3-hexylthiophene):[6,6]-phenylC61butyric-acid methyl-ester (P3HT:PCBM) and 40 nm PEDOT:PSS were deposited on ZnO thin film subsequently by solution spray coating.

Different volume of isopropyl alcohol was introduced into PEDOT:PSS to decrease the contact angle and obtain the optimum Marangoni flow.

The surface morphology and roughness of PEDOT:PSS films were characterized by atomic force microscopy with varied deposition temperature from 70°C to 160°C.

The improvement of power conversion efficiency (PCE) was attributed to the enhancement of vertical phase separation in PEDOT:PSS film, which improved the charge transfer in the bulk cell.

The highest PCE of spray-coated PSCs reached 2.80% after postannealing for 10 min.