Investigation on Nano-Self-Lubricant Coating Synthesized by Laser Cladding and Ion Sulfurization

Abstract EN

The composite processing between laser cladding and low temperature (300°C) ion sulfurization was applied to prepare wear resistant and self-lubricating coating.

The microstructure, morphology, phase composition, valence states, and wear resistance of the composite coating were investigated by scanning electron microscopy (SEM), atomic force microscope (AFM), X-ray diffraction (XRD), X-ray photoelectron spectroscope (XPS), and friction and wear apparatus.

The results indicate that the laser cladding Ni-based coatings and the maximum hardness of 46.5 HRC were obtained when the percent of pure W powder was 10%, composed of columnar dendrites crystals and ultrafine dendritic structure.

After ion sulfurization at 300°C for 4 h, the loose and porous composite coating is formed with nanograins and the granularity of all grains is less than 100 nm, which consists of γ-(Fe, Ni), M23C6 carbides, FeS, FeS2, and WS2.

Furthermore, the wear resistance of the composite coating is better than the laser cladding Ni55 + 10%W coating, and the friction coefficient and mass losses under the conditions of dry and oil lubrication are lower than those of laser cladding Ni55 + 10%W coating.