Modification of Leather Split by In Situ Polymerization of Acrylates

Abstract EN

Leather split, the byproduct of leather manufacture, possesses low utility value because it has loose weave of collagen fibers and weak mechanical strengths.

Herein, a practical and convenient method for increasing strengths of leather split was developed by one-step in situ polymerization.

The structures and properties of polyacrylate/leather split composites were systematically investigated.

The results suggested the monomers with an α-methyl and a proper straight-chain ester group, such as nBMA, can effectively modify the leather split.

For leather split with a thickness of 1.6 mm, the rational processes for preparation of polyacrylate/leather split composite are that monomer and split were stirred in a drum for 4 hours for full permeation and then the split was heated in anaerobic condition at 45°C for 30 min.

The tensile strength, tear strength, and elongation at break of the optimized PnBMA/split composite were 18.72 MPa, 62.73 N/mm, and 46.02%, respectively.

With these mechanical properties, the split after modification can be well used as leather for making shoes, bags, gloves, and clothing.