Nanostructured Fe2O3 Based Composites Prepared through Arc Plasma Method as Anode Materials in the Lithium-Ion Battery

Abstract EN

In the present work, a method combining arc plasma evaporation of a metal followed by oxidation in air was developed to produce nanosized metal oxide based composites in large scale.

As an example, Fe2O3 based nanocomposites were prepared through such a method.

With increasing the oxidation temperature, α-Fe2O3 content in the composites increases, while γ-Fe2O3 and residual α-Fe contents decrease.

As anode materials for lithium batteries, the electrochemical properties of nanosized Fe2O3 composites were tested.

It was found that the anode materials changed to tiny crystallites and then followed by grain growth during the galvanostatic charge/discharge cycles.

A capacity rising was observed for the composites obtained at 400°C and 450°C, which was more prominent with increasing the oxidation temperature.

Among these composites, the one obtained at 450°C showed the best performance: a specific capacity of 507.6 mAh/g remained after 150 cycles at a current density of 200 mA/g, much higher than that of the commercial nano-Fe2O3 powder (~180 mAh/g after 30 cycles).