Effect of Solvent, Dye-Loading Time, and Dye Choice on the Performance of Dye-Sensitized Solar Cells

Abstract EN

Anatase titania films with a thickness of up to 20 μm and deposited over a fluorine-doped tin-oxide substrate are impregnated with ruthenium dyes N-719 and N-749 using Dip and supercritical-fluid methods for the purpose of fabricating dye-sensitized solar cell devices.

The dyes are dissolved in different solvent mixtures, including supercritical carbon dioxide, as well as combinations of more traditional solvents including mixtures of acetonitrile, and t-butanol.

Analytical studies included thin-film analyzing and scanning electron microscopy to measure titania film thickness and porosity, UV-Vis spectroscopy to quantify dye concentration, and current-voltage device characterizations to assess energy conversion efficiency, as well as open-circuit voltage decay measurements and quantum efficiency to examine electron collection efficiency.

A significant result is that using the dye N-749 in a solvent that includes supercritical carbon dioxide leads to energy conversion efficiencies that are higher for devices with a thick 20 μm semiconductor film than for the case of devices with thinner films, including the 10 μm film thickness that is traditionally considered an upper threshold.

The supercritical-fluid method for the N-719 dye also enabled shorter impregnation duration than more conventional classical Dip Methods.