(Co,Mn)‎3O4 Spinel Coating for Protecting Metallic Interconnects Thermally Converted from an Electro-Codeposited Co-Mn3O4 Composite Coating

Abstract EN

Electro-codeposition was used to prepare the Co and Co-Mn3O4 precursor coatings on ferritic stainless steel E-brite.

Plated samples were exposed at 800°C in air for different durations (i.e., 10 min and 4 h) for thermal conversion of the deposited layer to a spinel coating.

The converted layer was characterized with scanning electron microscopy/energy-dispersive spectroscopy (SEM/EDS) and X-ray diffraction (XRD).

The results showed that after 10 min heat treatment, the plated Co layer was not fully oxidized and converted into a double-layer microstructure with an inner CoO layer and outer Co3O4 layer, while for the Co-Mn3O4 layer, the Mn3O4 particles were not completely dissolved into the oxide layer.

After 4 h of exposure, the surface layer was fully converted into the Co3O4 or (Co,Mn)3O4 spinel coating.

Though the Mn content in (Co,Mn)3O4 was relatively low, the Mn-doped spinel coating was advantageous over the pure cobalt spinel coating, as the thermally grown Cr2O3 scale at the coating/substrate interface was more compact and protective.

Co diffusion from the deposited layer into the alloy substrate was observed for both coatings.