Study of Antiultraviolet Asphalt Modifiers and Their Antiageing Effects

Abstract EN

Ultraviolet (UV) radiation causes serious ageing problems on pavement surface.

In recent years, different UV blocking materials have been used as modifiers to prevent asphalt ageing during the service life of the pavement.

In this study, three different materials have been used as modifiers in base asphalt to test their UV blocking effects: layered double hydroxides (LDHs), organomontmorillonite (OMMT), and carbon black (CB).

UV ageing was applied to simulate the ageing process and softening point, penetration, ductility, DSR (Dynamic Shear Rheometer) test, and Fourier Transform Infrared Spectroscopy (FTIR) test were conducted to evaluate the anti-UV ageing effects of the three UV blocking modifiers.

Physical property tests show that base asphalt was influenced more seriously by UV radiation compared to the modified asphalt.

DSR test results indicate that the complex modulus of asphalt before UV ageing is increased because of modifiers, while the complex modulus of base asphalt after UV ageing is higher than that of the modified asphalt, which shows that the UV blocking modifiers promote the antiageing effects of asphalt.

FTIR test reveals that the increment of carbonyl groups and sulfoxide groups of modified asphalt is less than that in base asphalt.

Tests indicate the best UV blocking effect results for samples with LDHs and the worst UV blocking effect results for samples with CB.