The Effect of Hydrofluoric Acid Surface Treatment on the Cyclic Fatigue Resistance of K3 NiTi Instruments

Abstract EN

The aim of this study was to investigate the effect of 50% hydrofluoric acid (HF) surface treatment on the cyclic fatigue resistance (CFR) of K3 NiTi instruments.

Twenty as-received and twenty HF-treated K3 NiTi instruments were compared in CFR.

The surface texture and fracture surface of two instrument groups were examined with a scanning electron microscope (SEM).

Additionally, any change of Ni and Ti composition from both instrument groups was investigated using energy dispersive spectrometry.

The results were analyzed with t-test.

The HF-treated K3 group showed statistically higher cyclic fatigue resistance than as-received K3 group (P<0.05).

HF-treated K3 instruments showed smoother and rounded surface compared to as-received K3 under SEM observation.

The fracture surfaces of both groups showed typical patterns of cyclic fatigue fracture.

There was no difference in surface Ni and Ti composition between two groups.

HF treatment of K3 instruments smoothed the file surface and increased the cyclic fatigue resistance, while it had no effect on surface ion composition and the file fracture pattern.