Effect of Microstructure on Hydrogen Diffusion in Weld and API X52 Pipeline Steel Base Metals under Cathodic Protection

Abstract EN

The aim of this research was to evaluate the influence of microstructure on hydrogen permeation of weld and API X52 base metal under cathodic protection.

The microstructures analyzed were of the API X52, as received, quenched, and annealed, and the welded zone.

The test was performed in base metal (BM), quenched base metal (QBM), annealed base metal (ABM), and weld metal (WM).

Hydrogen permeation flows were evaluated using electrochemical tests in a Devanathan cell.

The potentiodynamic polarization curves were carried out to evaluate the corrosion resistance of each microstructure.

All tests were carried out in synthetic soil solutions NS4 and NS4 + sodium thiosulfate at 25°C.

The sodium thiosulfate was used to simulate sulfate reduction bacteria (SRB).

Through polarization, assays established that the microstructure does not influence the corrosion resistance.

The permeation tests showed that weld metal had lower hydrogen flow than base metal as received, quenched, and annealed.