Study of the Corrosion Process of AZ91D Magnesium Alloy during the First Hours of Immersion in 3.5 wt.% NaCl Solution

Abstract EN

The AZ91D magnesium alloy was immersed in 3.5 wt.% NaCl solution at room temperature for times ranging from 1 minute up to 72 hours.

The aim was to investigate the evolution of the corrosion process using confocal laser scanning microscopy (CLSM), electrochemical impedance spectroscopy, and X-ray photoelectron spectroscopy.

The microstructure of the as-received alloy was initially characterized by optical microscopy and scanning electron microscopy (SEM).

The crystalline phases were identified by X-ray diffractometry.

The main phases were primary-α, eutectic-α, and β (Mg17Al12).

Vickers microhardness markings were made on the surface of one etched sample to facilitate the identification of the same region at each different immersion time, thus enabling the observation of the corrosion process evolution.

Corrosion initiates at the grain boundaries of the eutectic microconstituent and, then, propagates through primary α-grains.

The β-phase was less severely attacked.