Efficient Color Tuning of Upconversion Luminescence from Core-Shell Oxysulfide Nanoparticles

Abstract EN

The Y2O2S:Er3+@Y2O2S:Yb3+,Ho3+ core-shell up-conversion (UC) nanoparticles were successfully synthesized by the homogeneous co-precipitation method.

The Y2O2S:Er3+@Y2O2S:Yb3+,Ho3+ core-shell nanoparticles exhibit bright green emissions under 980 nm excitation, while the triple-ion doped Y2O2S:Er3+,Yb3+,Ho3+ sample presents mainly red emissions.

The intensity ratio of green-to-red emission of the core-shell and conventional triple-ion doped samples are 2.8 and 0.3, respectively.

Investigations on the UC mechanisms show that emissions from Er3+ and Ho3+ ions are achieved simultaneously in the core-shell nanoparticles.

This is due to the efficient energy transfers of Yb3+→Ho3+ within the shell layer and Yb3+→Er3+ between the shell and the core.

While the triple-ion doped Y2O2S: Er3+,Yb3+,Ho3+ sample exhibits mainly the emissions of Er3+ along with weak luminescence of Ho3+ ion.

Since the cross relaxation between Er3+ and Ho3+ ions in the Y2O2S:Er3+,Yb3+,Ho3+ nanoparticles can effectively suppress the emissions of Ho3+ ions.

Yet, in the core-shell structure, this cross relaxation can be successfully restrained in the core-shell structure where Er3+ is in the core and Ho3+ is in the shell.

Therefore, the construction of core-shell structure can improve the luminescence efficiency and provide a route for adjustment of emission color.