Direct Synthesis of MnO2 Nanorods on Carbon Cloth as Flexible Supercapacitor Electrode

Abstract EN

MnO2 nanorod/carbon cloth (MnO2/CC) composites were prepared through in situ redox deposition as freestanding electrodes for flexible supercapacitors.

The CC substrates possessing porous and interconnecting structures enable the uniform decoration of MnO2 nanorods on each fiber, thus forming conformal coaxial micro/nanocomposites.

Three-dimensional CC can provide considerable specific surface area for high mass loading of MnO2, and the direct deposition process without using polymeric binders enables reliable electrical connection of MnO2 with CC.

The effect of MnO2 decoration on the electrochemical performances was further investigated, indicating that the electrode prepared with 40 min deposition time shows high specific capacitance (220 F/g at a scan rate of 5 mV/s) and good cycling property (90% of the initial specific capacitance was maintained after 2500 cycles) in 1 M Na2SO4 aqueous solution.

This enhanced electrochemical performance is ascribed to the synergistic effect of good conductivity of carbon substrates as well as outstanding pseudocapacitance of MnO2 nanorods.

The obtained MnO2/CC compositing electrode with the advantages of low cost and easy fabrication is promising in applications of flexible supercapacitors.