Performance of Methyl-5-Benzoyl-2-Benzimidazole Carbamate (Mebendazole)‎ as Corrosion Inhibitor for Mild Steel in Dilute Sulphuric Acid

Abstract EN

The inhibitive effect of mebendazole (MBZ) on the corrosion of low-carbon steel in H2SO4 was investigated by gravimetric and electrochemical techniques as well as examination of specimens in the scanning electron microscope with attached energy dispersive X-ray spectrometer (EDS).

From gravimetric analysis, the highest inhibition efficiency of about 96.6% was obtained for 1.0 g of inhibitor in H2SO4 solution at 24 h, while with longer exposure times of between 72 to 120 h, the efficiencies averaged between 92 and 95%.

Tafel extrapolations from the polarization curves showed that 1.0 g MBZ gave a maximum inhibition efficiency of approximately 99% for the investigation conducted at 30°C, whereas 1.5 g of MBZ gave a maximum inhibition efficiency of about 85% at 60°C.

Inhibition efficiency increased with increasing concentrations of MBZ and decreased at elevated temperatures.

The inhibitive action was attributed to physical adsorption of MBZ species on the mild steel surface which followed the Langmuir adsorption isotherm.

MBZ performed as a mixed-type inhibitor on mild steel in dilute H2SO4.