Green synthesis and characterization of TiO2 nanoparticles using aloe Vera extract at different pH value

Abstract EN

The use of plant extracts for metal oxide nanoparticles synthesis has been extensively fludied as a safer alternative to ordinary methods.

The present work focused on the synthesis and characterization of Titanium dioxide nanoparticles (TiO2NPs) by eco-friendly green synthesis method.

The green synthesis was conducted at room temperature at different pH values (acidic, neutral, and basic) using Titanium tetrachloride (TiCl4) as a precursor and Aloe Vera leaves extract as a reducing agent to avoid the use of hazardous chemicals.

The characterization of TiO2NPs was carried out by UV-visible spectrophotometry, Fourier Transform Infrared spectroscopy (FTIR), X-ray Diffraction (XRD) and high-resolution transmission electron microscope (HRTEM).

The influence of pH on the cryflalline phase and size of the TiO2NPs was also fludied.

The results revealed that, the maximum absorption of acidic, neutral, and basic TiO2NPs were in the UV region at 318, 326 and 320 nm respectively.

The synthesized nanoparticles were spherical in shape and highly pure.

Formation of TiO2NPs was further confirmed by FTIR spectrum showed characteriflic peaks of Ti-O and Ti-O-Ti vibrations at 555 cm-1 and 1383 cm-1, respectively.

The average particle size of the acidic, neutral and basic TiO2NPs was 22.86±0.85, 15.83±0.902 and 13.3±0.68 nm, respectively.

Basic TiO2NPs were composed of only one cryflalline phase (anatase), neutral TiO2NPs composed of a mixture of anatase and rutile phases while acidic TiO2NPs composed of a mixture of anatase, rutile, and brookite phases.

Basic TiO2NPs exhibited the smallefl particle size with the purefl cryflalline phase, therefore, they are favored for further biomedical applications.