The effect of the waste of materials and carbon nanotube on the concrete incorporated with steel fibers
Joint Authors
Abd al-Hamid, Ala A.
Uthman, Farhad M.
Salim, Mayada H.
Source
Engineering and Technology Journal
Issue
Vol. 39, Issue 6 (30 Jun. 2021), pp.956-964, 9 p.
Publisher
Publication Date
2021-06-30
Country of Publication
Iraq
No. of Pages
9
Main Subjects
Topics
Abstract EN
The addition of agricultural and industrial solid wastes and nanomaterials to concrete combined with steel fibers to improve the mechanical and electrical properties of concrete was investigated.
This approach could be used in advanced applications in electromagnetic shielding and conductive concrete.
Steel fibers were used at 2% wt.
of sand and (induction furnace slag (EIF), carbon nanotube (CNT), steel wool fibers, prepared corn husks) at 0.5 and 1 wt.
% .
of cement.
Obtained results of using 1% for both carbon nanotube and steel wool with steel fibers in the mixture 4 and 6, respectively, showed the highest rates of compressive strength.
A similar result was shown when tested at 3, 7 and 28 days of age and compressive strength was 47.4MPa, 47.34MPa for the mixture 4 and 6 respectively.
The electrical conductivity and electrical resistance of the samples were measured at the age of 7 days.
The findings have also shown that adding steel wool as well as( CNT) gave the best results and the sample containing the furnace slag achieved satisfactory results as The addition of agricultural and industrial solid wastes and nanomaterials to concrete combined with steel fibers to improve the mechanical and electrical properties of concrete was investigated.
This approach could be used in advanced applications in electromagnetic shielding and conductive concrete.
Steel fibers were used at 2% wt.
of sand and (induction furnace slag (EIF), carbon nanotube (CNT), steel wool fibers, prepared corn husks) at 0.5 and 1 wt.
% .
of cement.
Obtained results of using 1% for both carbon nanotube and steel wool with steel fibers in the mixture 4 and 6, respectively, showed the highest rates of compressive strength.
A similar result was shown when tested at 3, 7 and 28 days of age and compressive strength was 47.4MPa, 47.34MPa for the mixture 4 and 6 respectively.
The electrical conductivity and electrical resistance of the samples were measured at the age of 7 days.
The findings have also shown that adding steel wool as well as( CNT) gave the best results and the sample containing the furnace slag achieved satisfactory results as well.
American Psychological Association (APA)
Salim, Mayada H.& Uthman, Farhad M.& Abd al-Hamid, Ala A.. 2021. The effect of the waste of materials and carbon nanotube on the concrete incorporated with steel fibers. Engineering and Technology Journal،Vol. 39, no. 6, pp.956-964.
https://search.emarefa.net/detail/BIM-1281554
Modern Language Association (MLA)
Salim, Mayada H.…[et al.]. The effect of the waste of materials and carbon nanotube on the concrete incorporated with steel fibers. Engineering and Technology Journal Vol. 39, no. 6 (2021), pp.956-964.
https://search.emarefa.net/detail/BIM-1281554
American Medical Association (AMA)
Salim, Mayada H.& Uthman, Farhad M.& Abd al-Hamid, Ala A.. The effect of the waste of materials and carbon nanotube on the concrete incorporated with steel fibers. Engineering and Technology Journal. 2021. Vol. 39, no. 6, pp.956-964.
https://search.emarefa.net/detail/BIM-1281554
Data Type
Journal Articles
Language
English
Notes
Includes bibliographical references : p. 963-964
Record ID
BIM-1281554