TEM image analysis of fracture surfaces of P91 steel and comparison with mechanical properties
Other Title(s)
تحليل صور TEM لأسطح الكسر لصلب P91 و مقارنتها بالخواص الميكانيكية
Joint Authors
Bin Isa, Muammar M.
Hamir, Abu Bakr Muhammad
Milovice, L. J.
Sharaf, Abd al-Salam M.
Source
Journal of Marine Sciences & Environmental Technologies
Issue
Vol. 7, Issue 2 (31 Dec. 2021), pp.88-96, 9 p.
Publisher
Alasmarya Islamic University Faculty of Marine Resources
Publication Date
2021-12-31
Country of Publication
Libya
No. of Pages
9
Main Subjects
Topics
Abstract AR
من أجل تحسين كفاءة الغلايات البخارية في محطات الطاقة الحديثة، يتعين على المهندسين استخدام المواد المعاصرة التي تتيح استغلال معايير أعلى، بشكل أساسي درجة حرارة و الضغط التشغيليين، مع مقاومة أشكال مختلفة من التأكل في نفس الوقت، لهذا الغرض، تم تطوير الفولاذ المارتنسيتي المعاصر 9-Cr12، و التي تسمي أو يرمز لها حديثا به M12-SHC ،E911 ،P92 ،P91 و SHM12.
تحلل الورقة البحث التجريبي على سلوك عينات الصلب الفريتي التجاري P91.
تم الحصول على بيانات السلوك على منطقة التأثير الحراري (HAZ) للوصلات الملحومة عن طريق اختبار العينات الناعمة الناتجة.
محاكاة مادة اللحام الجديدة.
تم إجراء مسح لاختبار الصلابة و خصائص الشد و معالجة عن-صور لأسطح الكسر في العينات.
أكد تحليل الصورة باستخدام ImagePro Plus نتائج الاختبارات التجريبية لحجم الحبيبات المقاسة بطريقة الدائرة و تم إيجاد علاقة مقارنة بين النسبة المئوية للكربيدات و الرواسب و الأقطار الصفائحية فيما يتعلق بدرجة الحرارة.
تحتوي المادة التي كان لها PWHT (المعالجة الحرارية اللاحقة للحام) على أعلى متوسط لقطر الصفائح، مما يشير إلى زيادة المتانة و انخفاض الصلابة مقارنة بالمعدن الأساسي (BM) و المواد التي بدون PWHT أي أن (كلما كان القطر الرقائقي أعلى، كانت صلابة المادة أصغر).
Abstract EN
In order to improve the efficiency of steam boilers in modern power plants, engineers have to use contemporary materials that enable exploitation at higher parameters, primarily operating temperature and pressure, with resistance to different forms of corrosion at the same time.
for that purpose, contemporary 9-12Cr martensitic steels, designated P91, P92, E911, VM12-SHC, and SHM12, were developed.
the paper analyzes experimental research on the behavior of commercial ferritic steel P91 samples.
behavior data on the heat affect zone (HAZ) of welded joints were obtained by testing smooth specimens produced by simulation of the new material welding.
a survey of testing hardness and tensile properties is given and images of the fracture surfaces of the samples were processed.
image analysis with Image Pro Plus confirmed experimental testing results for the grain size measured by the circle method and a comparative relationship between the percentage of carbides, precipitates, and lamellar diameters with respect to temperature is provided.
the material that was PWHT (post-weld heat treatment) has the highest mean value of lamellar diameter, which indicates increased toughness and decreased hardness compared to BM and material without PWHT i.e (the higher lamellar diameter, the smaller material hardness).
American Psychological Association (APA)
Hamir, Abu Bakr Muhammad& Milovice, L. J.& Bin Isa, Muammar M.& Sharaf, Abd al-Salam M.. 2021. TEM image analysis of fracture surfaces of P91 steel and comparison with mechanical properties. Journal of Marine Sciences & Environmental Technologies،Vol. 7, no. 2, pp.88-96.
https://search.emarefa.net/detail/BIM-1479196
Modern Language Association (MLA)
Hamir, Abu Bakr Muhammad…[et al.]. TEM image analysis of fracture surfaces of P91 steel and comparison with mechanical properties. Journal of Marine Sciences & Environmental Technologies Vol. 7, no. 2 (Dec. 2021), pp.88-96.
https://search.emarefa.net/detail/BIM-1479196
American Medical Association (AMA)
Hamir, Abu Bakr Muhammad& Milovice, L. J.& Bin Isa, Muammar M.& Sharaf, Abd al-Salam M.. TEM image analysis of fracture surfaces of P91 steel and comparison with mechanical properties. Journal of Marine Sciences & Environmental Technologies. 2021. Vol. 7, no. 2, pp.88-96.
https://search.emarefa.net/detail/BIM-1479196
Data Type
Journal Articles
Language
English
Notes
Includes bibliographical references : p. 95-96
Record ID
BIM-1479196