Structural and magnetic properties of bafe12-xalxo19 prepared by milling and calcinations

Abstract EN

Al substituted barium ferrite particles BaFe12-xAlxO19 with 0 ≤ x ≤ 0.8 have been prepared by ball milling method.

X-ray diffraction (XRD) has shown that the average crystallite size for all samples under investigation is in the range 66 – 76 nm.

Scanning electron microscopy (SEM) imaging indicates that the particle size is in the range 0.2 – 1.0 μm, which demonstrates that the particles are polycrystalline.

It was found that Al substitution does not significantly change the particle size of BaFe12-xAlxO19.

The magnetic properties have been investigated using a vibrating sample magnetometer, and the anisotropy field is estimated.

It was found that the coercivity of the samples increases from4.2 kOe to 6.0 kOe with increasing Al concentration from x = 0.0 to 0.8 due to the increase in the anisotropy field.

Interparticle interactions determined from the remnant magnetization data are found to be consistent with a reversal mechanism (demagnetizing like effect) for all samples examined.