Polyvinyl alcohol polyvinyl chloride (pva pvc) hollow fiber composite nanofiltration membranes for water treatment
Joint Authors
al-Sahli, Qusayy
Figoli, A.
al-Juburi, Sufyan
Elwan, Ghanim M.
Simone, S.
Drioli, E.
Source
Iraqi Journal of Chemical and Petroleum Engineering
Issue
Vol. 11, Issue 4 (31 Dec. 2010), pp.23-32, 10 p.
Publisher
University of Baghdad College of Engineering
Publication Date
2010-12-31
Country of Publication
Iraq
No. of Pages
10
Main Subjects
Topics
Abstract AR
تم تحضير نوعين من أغشية الألياف المجوفة و النانوية المكونة من PVA / PVC بواسطة طريقة الاكساء بالتغطيس في محلول PVA المائي المكون من بولي فنيل الكحول PVA، الماء و Fatty Alcohol (AEO9) Polyoxyethylene Ether و بنسب وزنية مئوية (0.05, 98.5, 4) على التوالي.
تم دراسة تأثير وقتين مختلفين لزمن اكساء أغشية الألياف المجوفة على التركيب الداخلي و الخارجي لأغشية ألياف PVA / PVC المركبة و النانوية باستخدام جهاز المجهر الالكتروني الماسح (SEM) و أيضا على أداء الأغشية في فصل المذابات و إنتاج الماء النقي.
وجد أن سمك طبقة الاكساء للألياف المحضرة من 19 % PVC كان رقيقا و بسمك µm6 بينما يدخل محلول الاكساء خلال السطح الخارجي و يسد التراكيب الاصبعية الشكل عندما يزداد زمن الاكساء من 30-20 ثانية.
بالإضافة إلى ذلك، تقل نفاذية الماء النقي و يزداد فصل المذابات بزيادة زمن الاكساء من 30-20 ثانية لكلا نوعي الألياف المجوفة النانوية.
إن الوزن الجزئيئ للمذابات المفصولة (MWCO) لأغشية ألياف PVA / PVC المجوفة النانوية كان ضمن مدى أغشية الفصل النانوية (Da 3000-2000).
Abstract EN
Two different polyvinyl alcohol / polyvinyl chloride (PVA / PVC) hollow fiber composite nanofiltration membranes were prepared after PVC hollow fiber membranes were coated using dip-coating method with PVA aqueous solution, which was composed of PVA, fatty alcohol polyoxyethylene ether (AEO9), and water [PVA / AEO9 / water (4:0.5:95.5) wt %].
Effect of two different PVC hollow fiber immersion times in coating solution were studied.
Cross-section, internal and external surfaces of the PVC hollow fibers and PVA / PVC composite nanofiltration membranes structures were characterized by scanning electron microscopy (SEM), pure water permeation flux and solutes rejection.
It was found that, the coating layer thickness on the outer surface of the 19 wt % PVC hollow fiber was thin and about (6μm), while the coating solution penetrates through the outer edge of the PVC hollow fiber and it looks like sponge-like structure with increase of the dip-coating time from 20 to 30 sec.
Besides, the pure water permeation flux decreases and solutes rejection increases with an increase of the coating time from 20 to 30 sec for the two PVA / PVC composite nanofiltration membranes.
Molecular weight cut-off (MWCO) of the PVA / PVC composite nanofiltration membranes were in the range of NF (i.e.
200-3000 Mw).
American Psychological Association (APA)
al-Sahli, Qusayy& Figoli, A.& al-Juburi, Sufyan& Elwan, Ghanim M.& Simone, S.& Drioli, E.. 2010. Polyvinyl alcohol polyvinyl chloride (pva pvc) hollow fiber composite nanofiltration membranes for water treatment. Iraqi Journal of Chemical and Petroleum Engineering،Vol. 11, no. 4, pp.23-32.
https://search.emarefa.net/detail/BIM-287172
Modern Language Association (MLA)
al-Sahli, Qusayy…[et al.]. Polyvinyl alcohol polyvinyl chloride (pva pvc) hollow fiber composite nanofiltration membranes for water treatment. Iraqi Journal of Chemical and Petroleum Engineering Vol. 11, no. 4 (Dec. 2010), pp.23-32.
https://search.emarefa.net/detail/BIM-287172
American Medical Association (AMA)
al-Sahli, Qusayy& Figoli, A.& al-Juburi, Sufyan& Elwan, Ghanim M.& Simone, S.& Drioli, E.. Polyvinyl alcohol polyvinyl chloride (pva pvc) hollow fiber composite nanofiltration membranes for water treatment. Iraqi Journal of Chemical and Petroleum Engineering. 2010. Vol. 11, no. 4, pp.23-32.